It has good tenacity,anti-earthquake capability. It has the higher machine strength and heat resistance,the better shock strength,the higher fusion point, the good property of molding process,high water absorption,the saturated water absorptivity is about 11%,and easy to fusion to phenols sulfate or formic acid， the low-temperature brittlenessis minus 20 degrees - 30 degrees.
Type:
PA(MC,PA6,PA66,PA1010),Sheet,Rod,Tube,Machined parts etc.
Main Properties & Application
High Strength and stiffness
Excellent abrasion resistance
Good sliding properties
Type and Specifications:
Type
Thickness (mm）
Length(mm)
Length(mm)
Sheet
≤ 100
500-1000
500-2000
Extruded tube
Diameter (mm)
200/300/1000/200
6-50
500-1000
3-24
Any length
Tube
Outer Diameter(mm)
Length(mm)
40-500
≤ 1000
Main Properties
Properties
Unit
Value
PA
PA6(cast)
Apparent Density
g/cm3
1.05-1.15
1.18
Tensile strength(min)
MPa
50-85
≥75-85
ElongationAt Break(min)
%
≥40-75
≥≥50-70
Dielectric Strength(min)
KV/mm
≥30
≥20
Dielectric Strength
C
-40-100C
-40-90C
PA is widely used for fiction ban,siding & transmission parts,pipe clamp,clutch part,gears,guide rails and other mechanical parts,etc